Title: Physical and mechanical properties of Ti1 - xSixN films
Authors: Vaz, F. 
Rebouta, L. 
Ramos, S. 
Cavaleiro, A. 
Silva, M. F. da 
Soares, J. C. 
Keywords: Rutherford back-scattering spectrometry; Silicon; Titanium; X-ray diffraction
Issue Date: 1998
Citation: Surface and Coatings Technology. 100-101:(1998) 110-115
Abstract: Ti1 - xSixN coatings with 0 <- x <- 0.30 and thicknesses ranging from 1.2 to 3.3 [mu]m, were deposited on to polished high-speed steel substrates by r.f. reactive magnetron sputtering. The atomic composition of the samples was measured by Rutherford backscatering spectrometry (RBS), and the texture was determined by X-ray diffraction (XRD). Great improvements in hardness and adhesion behaviour were obtained when compared to TiN. Hardness results and adhesion behaviour as a function of the Si content will be shown and discussed. The Ti0.85Si0.15N sample presented the best results with a hardness value of about 36 GPa and a critical load for total failure around 70 N.
URI: http://hdl.handle.net/10316/4327
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat 
file1905936f7e0f4aacb22e4fd4513c035c.pdf661.02 kBAdobe PDFView/Open
Show full item record

Page view(s) 50

309
checked on Jun 12, 2019

Download(s) 20

603
checked on Jun 12, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.