Título: | Ultra-low friction W–S–N solid lubricant coating | Autor: | Gustavsson, Fredrik Jacobson, Staffan Cavaleiro, Albano Polcar, Tomas |
Palavras-chave: | Tungsten disulfide; Ultra-low friction; Self-lubricant; Coating; Magnetron sputtering | Data: | 15-Out-2013 | Editora: | Elsevier | Citação: | GUSTAVSSON, Fradrik [et. al] - Ultra-low friction W–S–N solid lubricant coating. "Surface and Coatings Technology". ISSN 0257-8972. Vol. 232 (2013) p. 541-548 | Título da revista, periódico, livro ou evento: | Surface and Coatings Technology | Volume: | 232 | Resumo: | W–S–N films were deposited by reactive magnetron sputtering from WS2 target in Ar/N2 atmosphere. Besides the standard evaluation of composition, structure, morphology, hardness and cohesion/adhesion, the core objective of this paper was to analyze coating tribological behavior. The chemical composition was 34 at.% N, 12 at.% O, 29 at.% W and 25 at.% S, and the as-deposited films were completely amorphous. The film thickness was 2.3 μm, including the approximately 300-nm thick adhesion improving titanium interlayer. The friction coefficient was lower than 0.003 when sliding in dry nitrogen. The coating showed remarkable wear resistance surviving more than 2 million laps on pin-on-dics. The excellent friction properties were attributed to the formation of a thin tungsten disulfide tribofilm on the top of the wear track of the coating and on the counterpart surface. Moreover, the coating showed ability to replenish damaged areas with solid lubricant. We demonstrated that a structural transformation of the coating from an amorphous-like to a gradient quasi-ordered structure and an ordered transfer layer formation improved mechanical properties and radically decreased friction and wear. | URI: | https://hdl.handle.net/10316/27273 | ISSN: | 0257-8972 | DOI: | 10.1016/j.surfcoat.2013.06.026 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Ultra-low friction W-S-N solid lubricant coating.pdf | 1.28 MB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
57
Visto em 23/set/2024
Citações WEB OF SCIENCETM
5
53
Visto em 2/set/2024
Visualizações de página 50
571
Visto em 24/set/2024
Downloads 50
490
Visto em 24/set/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.