Title: Indentation and scratch testing of DLC-Zr coatings on ultrafine-grained titanium processed by high-pressure torsion
Authors: Wang, Chuan Ting 
Escudeiro, Ana 
Polcar, Tomas 
Cavaleiro, Albano 
Wood, Robert J. K. 
Gao, Nong 
Langdon, Terence G. 
Keywords: High-pressure torsion; Titanium; DLC-Zr coatings; Adhesion; Bio-implants
Issue Date: 30-Aug-2013
Publisher: Elsevier
Citation: WANG, Chuan Ting [et al.] - Indentation and scratch testing of DLC-Zr coatings on ultrafine-grained titanium processed by high-pressure torsion. "Wear". ISSN 0043-1648. Vol. 306 Nº. 1-2 (2013) p. 304-310
Serial title, monograph or event: Wear
Volume: 306
Issue: 1-2
Abstract: High-pressure torsion was employed to refine the microstructure of grade 2 Ti under an imposed pressure of 3.0 GPa at room temperature. The microhardness of grade 2 Ti increased from 1.82 GPa for the coarse grain state to 3.05 GPa after high-pressure torsion processing, where this value is very close to the hardness of the Ti–6Al–4V alloy. Subsequently, several diamond-like carbon (DLC) coatings with thicknesses of ∼1.4 μm were deposited on as-received Ti, high-pressure torsion processed Ti and Ti–6Al–4V samples via physical vapour deposition. Both indentation and scratch tests showed a much improved adhesion of DLC-7Zr, DLC:H-7Zr and DLC-9Zr coatings with high-pressure torsion processed Ti as the substrate by comparison with the same coatings on coarse-grained Ti. The results suggest that commercial pure Ti processed by high-pressure torsion and coated with a diamond-like carbon coating provides a potential candidate material for bio-implant applications.
URI: http://hdl.handle.net/10316/27171
ISSN: 0043-1648
DOI: 10.1016/j.wear.2012.12.033
Rights: openAccess
Appears in Collections:I&D CEMMPRE - Artigos em Revistas Internacionais
FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat
Indentation and Scratch Testing of DLC-Zr coatings.pdf882.84 kBAdobe PDFView/Open
Show full item record

SCOPUSTM   
Citations

38
checked on Nov 11, 2022

WEB OF SCIENCETM
Citations 5

41
checked on Aug 2, 2022

Page view(s) 50

388
checked on Nov 28, 2022

Download(s) 50

684
checked on Nov 28, 2022

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.