dc.contributor.authorWang, Chuan Ting-
dc.contributor.authorEscudeiro, Ana-
dc.contributor.authorPolcar, Tomas-
dc.contributor.authorCavaleiro, Albano-
dc.contributor.authorWood, Robert J. K.-
dc.contributor.authorGao, Nong-
dc.contributor.authorLangdon, Terence G.-
dc.date.accessioned2014-10-01T11:12:30Z-
dc.date.available2014-10-01T11:12:30Z-
dc.date.issued2013-08-30-
dc.identifier.citationWANG, Chuan Ting [et al.] - Indentation and scratch testing of DLC-Zr coatings on ultrafine-grained titanium processed by high-pressure torsion. "Wear". ISSN 0043-1648. Vol. 306 Nº. 1-2 (2013) p. 304-310por
dc.identifier.issn0043-1648-
dc.identifier.urihttps://hdl.handle.net/10316/27171-
dc.description.abstractHigh-pressure torsion was employed to refine the microstructure of grade 2 Ti under an imposed pressure of 3.0 GPa at room temperature. The microhardness of grade 2 Ti increased from 1.82 GPa for the coarse grain state to 3.05 GPa after high-pressure torsion processing, where this value is very close to the hardness of the Ti–6Al–4V alloy. Subsequently, several diamond-like carbon (DLC) coatings with thicknesses of ∼1.4 μm were deposited on as-received Ti, high-pressure torsion processed Ti and Ti–6Al–4V samples via physical vapour deposition. Both indentation and scratch tests showed a much improved adhesion of DLC-7Zr, DLC:H-7Zr and DLC-9Zr coatings with high-pressure torsion processed Ti as the substrate by comparison with the same coatings on coarse-grained Ti. The results suggest that commercial pure Ti processed by high-pressure torsion and coated with a diamond-like carbon coating provides a potential candidate material for bio-implant applications.por
dc.language.isoengpor
dc.publisherElsevierpor
dc.rightsopenAccesspor
dc.subjectHigh-pressure torsionpor
dc.subjectTitaniumpor
dc.subjectDLC-Zr coatingspor
dc.subjectAdhesionpor
dc.subjectBio-implantspor
dc.titleIndentation and scratch testing of DLC-Zr coatings on ultrafine-grained titanium processed by high-pressure torsionpor
dc.typearticlepor
degois.publication.firstPage304por
degois.publication.lastPage310por
degois.publication.issue1-2por
degois.publication.titleWearpor
dc.relation.publisherversionhttp://www.sciencedirect.com/science/article/pii/S0043164812004619por
dc.peerreviewedYespor
dc.identifier.doi10.1016/j.wear.2012.12.033-
degois.publication.volume306por
item.openairetypearticle-
item.languageiso639-1en-
item.openairecristypehttp://purl.org/coar/resource_type/c_18cf-
item.cerifentitytypePublications-
item.grantfulltextopen-
item.fulltextCom Texto completo-
Appears in Collections:I&D CEMMPRE - Artigos em Revistas Internacionais
FCTUC Eng.Mecânica - Artigos em Revistas Internacionais
Files in This Item:
File Description SizeFormat
Indentation and Scratch Testing of DLC-Zr coatings.pdf882.84 kBAdobe PDFView/Open
Show simple item record

SCOPUSTM   
Citations

41
checked on Mar 25, 2024

WEB OF SCIENCETM
Citations 5

45
checked on Mar 2, 2024

Page view(s) 50

451
checked on Mar 26, 2024

Download(s) 50

746
checked on Mar 26, 2024

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.