Título: | A Comparative Study of Different Poly (Lactic Acid) Bio-Composites Produced by Mechanical Alloying and Casting for Tribological Applications | Autor: | Al Abir, Anzum Trindade, Bruno |
Palavras-chave: | PLA-based bio-composites; mechanical alloying; casting; hardness; friction; wear | Data: | 15-Fev-2023 | Editora: | MDPI | Projeto: | UIDB/00285/2020 LA/P/0112/2020 |
Título da revista, periódico, livro ou evento: | Materials | Volume: | 16 | Número: | 4 | Resumo: | The aim of this study was to fabricate different self-lubricating poly (lactic acid)-based bio-composites reinforced with mono- and multi-fillers of carbon fibers, graphene nanoparticles, and a soft Sn-based brazing alloy (Sn89-Zn8-Bi3) using a two-step process consisting of mechanical alloying followed by casting. The results showed that the incorporation of the different fillers on the PLA surface by mechanical alloying was quite homogenous. The volume ratio between the PLA and the fillers was 1:0.02, respectively. The PLA sample reinforced with short carbon fibers and graphene nanoparticles presented the highest hardness (84.5 Shore D, corresponding to a 10% increase compared to PLA) and the lowest specific wear rate (1.5 × 10-4 mm3/N·m, one order of magnitude lower than PLA). With regard to the coefficient of friction, the lowest value was obtained for the sample reinforced with graphene (0.43, corresponding to a decrease of 12% compared to PLA). | URI: | https://hdl.handle.net/10316/114027 | ISSN: | 1996-1944 | DOI: | 10.3390/ma16041608 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
A-Comparative-Study-of-Different-Poly-Lactic-Acid-BioComposites-Produced-by-Mechanical-Alloying-and-Casting-for-Tribological-ApplicationsMaterials.pdf | 28.56 MB | Adobe PDF | Ver/Abrir |
Visualizações de página
29
Visto em 8/mai/2024
Downloads
16
Visto em 8/mai/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Este registo está protegido por Licença Creative Commons