Título: | Environmental effect on the fatigue crack propagation of AM TiAl6V4 alloy specimens | Autor: | Borrego, L. P. Jesus, J. de Ferreira, J. A. M. Costa, J. D. Capela, C. |
Palavras-chave: | Additive manufacturing; corrosion-fatigue; crack propagation; Titanium TiAl6V4 alloy | Data: | 2019 | Projeto: | project no. 028789, financed by the European Regional Development Fund (FEDER), through the Portugal-2020 program (PT2020), under the Regional Operational Program of the Center (CENTRO-01-0145-FEDER-028789) project no. 042536-18/SI/2018, financed by European Funds, through program COMPETE2020, under the Eureka smart label S0129-AddDies Foundation for Science and Technology IP/MCTES through national funds (PIDDAC) |
Título da revista, periódico, livro ou evento: | Procedia Structural Integrity | Volume: | 17 | Resumo: | industry, because of its high strength, low weight and excellent biocompatibility. Most of these components work under environmentally assisted cyclic loading, i.e. under corrosion-fatigue. Fatigue performance of additive manufactured alloys is significantly influenced by the porosities, residual stresses, which can be reduced by optimizing the process parameters, thermal treatments or hot isostatic pressing (HIP). Those parameters can also influence significantly to the propagation of cracks under corrosion-fatigue, but the understanding of this subject still needs significant research work. This paper presents the results of a fatigue crack propagation study in titanium TiAl6V4 specimens produced by selective laser melting (SLM), under corrosive ambient. The environment solutions studied were: artificial saliva and 3.5%wt NaCl solution. Tests were performed using standard 6 mm thick compact specimens (CT) tested at R=0.05 and with frequency 10 Hz. The main objective was to study the effect of the environment solution on da/dN-ΔK curves and on the fatigue failure mechanisms. Current work shows a very important accelerating effect on the crack nucleation and fatigue crack propagation for tests under corrosion ambient, particularly for 3.5%wt NaCl solution. Fatigue path shows an irregular path. Secondary cracking was observed in air, but not detected in corrosive ambient. | URI: | https://hdl.handle.net/10316/101627 | ISSN: | 24523216 | DOI: | 10.1016/j.prostr.2019.08.075 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
1-s2.0-S245232161930280X-main.pdf | 1.04 MB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
3
Visto em 17/nov/2022
Citações WEB OF SCIENCETM
3
Visto em 2/mai/2023
Visualizações de página
92
Visto em 16/out/2024
Downloads
51
Visto em 16/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Este registo está protegido por Licença Creative Commons