Título: | Tribological behaviour of C-alloyed transition metal dichalcogenides (TMD) coatings in different environments | Autor: | Evaristo, Manuel Polcar, Tomas Cavaleiro, Albano |
Data: | 2008 | Citação: | International Journal of Mechanics and Materials in Design. 4:2 (2008) 137-143 | Resumo: | Abstract W-S-C films were deposited by non-reactive sputtering from a carbon target incrusted with WS2 pellets in the eroded zone. This process allows depositing coatings with a wide range of compositions, with a precise control of their carbon content. Before the deposition, a Ti interlayer was interposed between the film and the substrate to improve the final adhesion. The carbon content in W-S-C system was varied from 29 at.% to 70 at.%, which led to an hardness enhancement from 4 GPa up to 10 GPa where the maximum hardness was reached in films with a carbon content between 40 at.% and 50 at.%. The tribological behaviour of the coatings was evaluated by pin-on-disk testing, in environments with different humidity levels. Generally, the tribological performance of W-S-C coatings in environments with moderate to high humidity is better for coatings with high carbon content. Friction coefficients, as 0.05 or lower could be reached at low humidity ranges (<7%) to all compositions. However, for higher humidity values, friction coefficient increased up to 0.30 in the W-S-C film with low carbon content whereas it was kept approximately constant for the others compositions. | URI: | https://hdl.handle.net/10316/7652 | DOI: | 10.1007/s10999-007-9034-2 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Mostrar registo em formato completo
Citações SCOPUSTM
19
Visto em 23/set/2024
Visualizações de página 50
582
Visto em 1/out/2024
Downloads 20
896
Visto em 1/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.