Title: Property change in ZrNxOy thin films: effect of the oxygen fraction and bias voltage
Authors: Vaz, F. 
Carvalho, P. 
Cunha, L. 
Rebouta, L. 
Moura, C. 
Alves, E. 
Ramos, A. R. 
Cavaleiro, A. 
Goudeau, Ph. 
Rivière, J. P. 
Keywords: Oxygen fraction; Bias voltage
Issue Date: 2004
Citation: Thin Solid Films. 469-470:(2004) 11-17
Abstract: The main purpose of this work consists on the preparation of single layered zirconium oxynitride, ZrNxOy, thin films, deposited by rf reactive magnetron sputtering. The depositions were carried out by varying the process parameters such as substrate bias voltage and flow rate of the reactive gases. Independently of O content, the samples prepared with oxygen fractions revealed crystalline structures basically constituted by face centred cubic ZrN grains. Atomic force microscopy (AFM) observation showed lower values of surface roughness for low oxygen fractions and a second region where roughness grows significantly, corresponding to the highest oxygen fractions. Ion bombardment promoted a continuous smoothing of the surface up to a bias voltage of -66 V. At a bias voltage of -75 V, roughening is again observed. The small increase of film hardness in low oxygen fractions ZrNxOy films was attributed to lattice distortions occurring as a result of the possible oxygen incorporation within the ZrN lattice and also grain size reduction. Residual stresses appeared to be an important parameter to explain the observed behaviour, namely in the group of samples prepared with variation in the bias voltage. Regarding colour variations, it was observed a clear dependence of the obtained colorations with oxygen fraction.
URI: http://hdl.handle.net/10316/4248
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat 
filef7813df68f464c849561dd45bfecf843.pdf487.66 kBAdobe PDFView/Open
Show full item record

Page view(s) 20

472
checked on Jun 12, 2019

Download(s) 50

312
checked on Jun 12, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.