Title: Revestimento de fios de Nitinol - uma aproximação para a reparação de dispositivos médicos
Authors: Caiano, Ana Catarina Ribeiro 
Orientador: Ramos, Ana Sofia Figueira
Keywords: Fios NiTi; filmes finos multicamada; Ni/Al; pulverização catódica; SEM; ignição; NiTi wires; multilayer thin films; Ni/Al; sputtering; SEM; ignition
Issue Date: 23-Sep-2014
Place of publication or event: Coimbra
Abstract: O presente trabalho visa o revestimento de fios de Nitinol com filmes finos multicamada reativos, com o intuito de empregar o calor libertado pela reação autossustentada das multicamadas numa aplicação inovadora, nomeadamente na reparação de fissuras em dispositivos médicos. Para tal, foi selecionado o sistema Ni-Al, pois os filmes multicamada Ni/Al equiatómicos apresentam um bom compromisso entre custo e entalpia de reação. Filmes finos de Ni/Al com períodos de modelação entre 5 e 50 nm foram depositados por pulverização catódica d.c. magnetrão sobre fios de NiTi com diâmetros iguais a 0,4 e 0,7 mm. Após deposição, a composição química global e a rugosidade superficial dos filmes foram avaliadas. A secção transversal das multicamadas foi observada em detalhe por microscopia eletrónica de varrimento e a estrutura cristalina estudada por difração de raios X. Por fim foram realizados testes de ignição de modo a averiguar a capacidade de autopropagação da reação nos filmes em estudo. O trabalho efetuado permitiu comprovar a possibilidade de revestir superfícies curvas, como a dos fios, com filmes finos multicamada nanométricos. Os filmes produzidos apresentam uma espessura constante que acompanha a superfície dos fios, possuem rugosidade reduzida e as camadas de Ni e de Al são bem distintas e identificáveis. Mesmo em condições de deposição com arrefecimento ineficiente dos substratos, foram produzidos filmes multicamada com espessura total na ordem dos 4 μm. Nos testes de ignição foi apenas possível propagar a reação em filmes Ni/Al destacados do substrato com períodos de modelação iguais ou superiores a 14 nm.
This paper aims at coating Nitinol wires with reactive multilayer thin films in order to use the heat released by the self-sustaining reaction of the multilayers on an innovative application, particularly for repairing cracks in medical devices. The Ni-Al system was selected because the equiatomic Ni/Al multilayer films exhibit a good compromise between cost and heat of reaction. Ni/Al thin films with modulation periods between 5 and 50 nm were deposited by dc sputtering magnetron onto NiTi wires with diameters of 0.4 and 0.7 mm. After deposition, the films’ overall chemical composition and surface roughness were evaluated. The cross section of the multilayers was observed in detail by scanning electron microscopy and the crystal structure was studied by X-ray diffraction. Finally, ignition tests were conducted in order to investigate the capability of triggering self-propagating reactions in the films under study. The work carried out proved the possibility of coating curved surfaces, such as wires, with nanometric multilayer thin films. The films have a constant thickness which follows the surface of the wires, have a reduced roughness, and the Ni and Al nanolayers are distinct and perfectly identifiable. Even under deposition conditions with inefficient substrates’ cooling, multilayer films were produced with a total thickness close to 4 m. In the ignition tests it was only possible to propagate the reaction on free-standing Ni/Al films with modulation periods greater than or equal to 14 nm.
Description: Dissertação de Mestrado em Engenharia de Materiais apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
URI: http://hdl.handle.net/10316/38828
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado
FCTUC Eng.Mecânica - Teses de Mestrado

Files in This Item:
File Description SizeFormat
Tese_AnaCaiano.pdf4.12 MBAdobe PDFView/Open
Show full item record

Page view(s)

151
checked on Aug 18, 2022

Download(s)

5
checked on Aug 18, 2022

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.