Título: | Research on the Specific Heat Capacity of PBX Formulations Based on RDX | Autor: | Chaves, Flávio Rodrigues Góis, José Carlos |
Palavras-chave: | Heat capacity; DSC; RDX; HTPB; DOS; IPDI | Data: | 2016 | Editora: | Elsevier | Título da revista, periódico, livro ou evento: | Journal of Aerospace Technology and Management | Volume: | 8 | Número: | 3 | Resumo: | The experimental results of specific heat capacity of 2 plastic bonded explosives formulations based on 1,3,5-trinitroperhydro-1,3,5-triazine, using differential scanning calorimetry thermal analysis, and the theoretical ones calculated with the specific heat capacity and mass fraction of individual compounds are compared for a temperature range between 340 and 410 K. Apart the filler, the plastic bonded explosives composition includes the binder based on hydroxyl-terminated polybutadiene, the plasticizer bis (2-ethylhexyl) sebacate and the curing agent isophorone diisocyanate. The experimental and theoretical results showed a better approach when no curing agent is added. Without curing agent, the specific heat capacity of plastic bonded explosives increases linearly with temperature. When plastic bonded explosive is cured, the specific heat capacity is nearly constant until 380 K and decreases linearly for higher temperature values. These results suggest that phase change requires adjusting parameters to different heating rates in order to describe adequately the experimental data. | URI: | https://hdl.handle.net/10316/108642 | ISSN: | 2175-9146 | DOI: | 10.5028/jatm.v8i3.655 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Nacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Research on the specific heat capacity of PBX formulations based on RDX.pdf | 220.59 kB | Adobe PDF | Ver/Abrir |
Visualizações de página
78
Visto em 17/jul/2024
Downloads
33
Visto em 17/jul/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Este registo está protegido por Licença Creative Commons