Title: Physical, structural and mechanical characterization of Ti1-xSixNy films
Authors: Vaz, F. 
Rebouta, L. 
Ramos, S. 
Silva, M. F. da 
Soares, J. C. 
Keywords: Hard coatings; Titanium and silicon nitride; Grain size; Texture
Issue Date: 1998
Citation: Surface and Coatings Technology. 108-109:1-3 (1998) 236-240
Abstract: Within the frame of this work, Ti1-xSixNy hard coatings with 0<=x<=0.37 and thicknesses ranging from 1.2 to 3.5 [mu]m, were prepared by r.f. reactive magnetron sputtering in an Ar/N2 gas mixture. X-ray diffraction and Fourier analysis of X-ray profiles were used to investigate the structure and grain size, and its correlation with hardness behaviour, as a function of the Si content, bias voltage and working gas (argon) flow rate. In this respect, the results show that a double cubic phase of NaCl type was developed with lattice parameters of 4.18 and 4.30 Ã…, revealing the (111) orientation for low Si content (x=0.05), (220) for intermediate Si contents (0.13<=x<=0.22) and (200) for the highest Si contents (0.30<=x<=0.37). Regarding the results of ultramicrohardness tests, and although all samples with 0.05<=x<=0.30 present a hardness value higher than 30 GPa, the Ti0.85Si0.15N1.03 revealed the highest hardness value, around 47 GPa, which is more than twice as high as that of common TiN. Furthermore, the study of hardness as a function of the applied bias voltage revealed that best results are achieved between -50 and 0 V. The variation in hardness as a function of the argon flow showed that best results in hardness are obtained when working with flow rates around 110 cm3/min.
URI: http://hdl.handle.net/10316/4325
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat 
file488fc00795f142a8ae2480723f7a35fb.pdf145.59 kBAdobe PDFView/Open
Show full item record

Page view(s)

92
checked on Jun 12, 2019

Download(s) 50

229
checked on Jun 12, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.