Please use this identifier to cite or link to this item: http://hdl.handle.net/10316/38988
Title: Análise da influência do fenómeno de fecho de fenda na propagação de fendas por fadiga na liga de alumínio AA7050
Other Titles: Analysis of crack closure influence on fatigue crack propagation in the AA7050 aluminum alloy
Authors: Nunes, Tiago Pedro Alves Serra 
Orientador: Costa, José Domingos Moreira da
Borrego, Luís Filipe Pires
Keywords: Liga de Alumínio; Fadiga; Propagação de Fendas; Fecho de fenda; Aluminum Alloys; Fatigue; Crack Growth; Crack Closure
Issue Date: 27-Jul-2015
Place of publication or event: Coimbra
Abstract: As ligas de alumínio são utilizadas numa vasta gama de aplicações, destacando-se a indústria aeronáutica. O estudo das solicitações aplicadas aos componentes fabricados nestes materiais é, por isso, extremamente importante. Esta dissertação teve como objetivos principais a análise da propagação de fendas por fadiga, na liga de alumínio AA7050-T6, quando sujeita a diferentes tipos de carregamento, além do estudo da influência do fenómeno do fecho de fenda na evolução dessa mesma propagação. Para tal, efetuaram-se ensaios em provetes MT com vista à obtenção das curvas de propagação, tendo sido posteriormente analisadas e comparadas, a fim de compreender o efeito do fecho de fenda aquando da aplicação de sobrecargas e da variação da razão de tensões. Nesta análise, o parâmetro de fecho de fenda, U, foi relacionado com a gama do fator de intensidade de tensões, K, para os vários tipos de ensaios. Foi possível concluir, após a realização dos ensaios e o tratamento dos dados subsequentes, que a velocidade de propagação aumenta diretamente com a razão de tensões, além de se verificar que as sobrecargas únicas fazem retardar o crescimento de fenda, para razões de tensões mais elevadas do ciclo de base. Já a aplicação de sobrecargas periódicas, no presente trabalho, levou a dados inconclusivos.
Aluminum alloys are used in various applications, in which the aeronautical industry is the most significant. The study of the loads applied on the components incorporating this kind of materials is, therefore, extremely important. This dissertation has, by primary objectives, the analysis of the fatigue crack growth on the AA7050-T6 aluminum alloy, when it is loaded in different ways, as well as the study of the influence crack closure has in this very growth. For that being, tests were performed on MT specimens, which allowed the obtainment of the propagation curves, later analyzed and compared, so that the effect of crack closure, during the application of overloads and the variation of the middle tension, can be understood. This was achieved by the relating the crack closure parameter, U, with the stress intensity factor range, DK, for all the executed tests. After the tests and the processing of its data, it was confirmed that an increasing of the middle-tension leads to the quickening of the fatigue crack growth. Also, the single overloads could produce a greater retardation of the crack growth, during a based cycle, for lower middle-tensions. Finally, the periodic overload tests were considered inconclusive.
Description: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
URI: http://hdl.handle.net/10316/38988
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado
FCTUC Eng.Mecânica - Teses de Mestrado

Show full item record

Page view(s) 50

532
checked on Sep 27, 2022

Download(s)

158
checked on Sep 27, 2022

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.