Utilize este identificador para referenciar este registo: https://hdl.handle.net/10316/99961
Título: Specific features of structural, magnetic, Raman and Mössbauer: Properties of La 0.57 Nd 0.10 Sr 0.18 Ag 0.15 FeO 3 ferrite nanoparticules
Autor: Issaoui, F.
Issaoui, H.
Dhahri, E.
Costa, Benilde F.O. 
Nogueira, Bernardo Albuquerque 
Fausto, Rui 
Palavras-chave: Solid-state synthesis; Ferrite nanoparticles; Magnetic properties; X-ray diffraction; Raman spectroscopy; Mössbauer spectroscopy
Data: 6-Abr-2021
Editora: Elsevier
Projeto: UID/04564/2020 
UIDB/00313/2020 
UIDP/00313/2020 
Título da revista, periódico, livro ou evento: Journal of Molecular Structure
Volume: 1238
Resumo: This article reports on a detailed study of the structural, spectroscopic and magnetic properties of La 0.57 Nd 0.10 Sr 0.18 Ag 0.15 FeO 3 (LNSAFO) ferrite nanoparticles, which were prepared using the solid state tech- nique. The Rietveld analysis of the powder X-ray diffractograms indicated that the material crystalizes in an orthorhombic structure, Pnma space group. Scanning electron microscopy (SEM) measurements showed that all particles have almost spherical shapes, and are characterized by a distribution of rela- tively narrow particle sizes. The average diameter of the particles was estimated within the 25–45 nm range by three different methods (SEM, and from the XRD data using the Debye-Scherer and Williamson–Hall models).The elemental composition of the synthesized material has been investigated by energy dis- persive spectroscopy (EDS), which confirmed the presence of all expected elements in stoichiometries matching those of the precursor oxides of the synthesized perovskite. Raman spectroscopy measure- ments revealed that the studied sample had a considerable degree of crystallinity, in agreement with the X-ray diffraction data. Finally, the magnetic properties of the studied compound have been investi- gated by studying the variation of the magnetization as a function of temperature in both the ZFC (zero field cooled) and FC (field cooled) modes. A blocking temperature ( T B ) of around 100 K was observed.
URI: https://hdl.handle.net/10316/99961
ISSN: 0022-2860
DOI: 10.1016/j.molstruc.2021.130344
Direitos: embargoedAccess
Aparece nas coleções:I&D CQC - Artigos em Revistas Internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato
1-s2.0-S0022286021004774-main.pdf2.12 MBAdobe PDFVer/Abrir
Mostrar registo em formato completo

Citações SCOPUSTM   

1
Visto em 26/fev/2024

Citações WEB OF SCIENCETM

1
Visto em 2/mar/2024

Visualizações de página

91
Visto em 26/mar/2024

Downloads

16
Visto em 26/mar/2024

Google ScholarTM

Verificar

Altmetric

Altmetric


Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.