Title: Avaliação da degradação das propriedades mecânicas de juntas soldadas com o aumento da temperatura
Other Titles: EVALUATION OF THE DEGRADATION OF THE MECHANICAL PROPERTIES OF WELDS WITH THE INCREASE OF TEMPERATURE
Authors: Nunes, Caline Milú Martins
Orientador: Santiago, Aldina Maria da Cruz
Craveiro, Hélder David da Silva
Keywords: aço S355J2; juntas soldadas; fatores de redução; propriedades mecâncias; análise microestrutural; steel S355J2; welded joints; reduction factors; mechanical properties; microstructural analysis
Issue Date: 9-Dec-2021
Serial title, monograph or event: Avaliação da degradação das propriedades mecânicas de juntas soldadas com o aumento da temperatura
Place of publication or event: DEC-FCTUC
Abstract: Foi realizado um programa de pesquisa experimental na Universidade de Coimbra, a fimde avaliar a degradação das propriedades mecânicas de juntas soldadas de topo fabricadas com oaço S355 J2.A avaliação assentou na realização de testes de caracterização mecânica e numacaracterização microestrutural.Os ensaios mecânicos de caraterização a elevadas temperaturas foram realizados emregime transiente.A caracterização microestrutural e medidas de dureza foram realizadas para explicar ocomportamento de tração dos provetes após a exposição a altas temperaturas, recorrendo a técnicasde microscopia ótica para realizar observações metalográficas.Os resultados foram comparados. Esta comparação foi realizada por meio de análises deresultados de diagramas de tensão e extensão de ensaios realizados em provetes, confrontando osparâmetros de resistência do aço, no que se refere ao comportamento do material em questão. Apartir dos resultados deste estudo, foi possível compreender o comportamento dos provetesmetálicos, quando expostos a situações de aquecimento.Com base nas curvas de tensão-deformação em uma temperatura específica, determinouseos parâmetros mecânicos e fatores de redução e foram comparados com os resultados obtidoscom diversos autores e com as normas EN 1993 1-2, Australian Standard AS 4100 (1998) (CódigoAustraliano) e British Standard BS 5950-8 (Código Britânico).Este estudo revelou que a tensão de cedência das soldaduras diminuem gradualmente como aumento da temperatura. A comparação mostrou uma semelhança entre a curva dos fatores deredução da tensão de cedência relativa ao aço em estudo associados a extensões de 1.5 e 2.0% e acurva preconizada pela EN 1993-1-2:2010 (2010) para aços laminados a quente da classe 4utilizada. Enquanto que a curva dos fatores de redução da tensão de cedência relativa ao aço emestudo associados a extensões de 0.2%, e 0.5% assemelhou-se à curva preconizada pela normabritânica (BS 5950-8).
An experimental research program was carried out at the University of Coimbra, in order toevaluate the degradation of the mechanical properties of butt welded joints manufactured with S355 J2steel.The evaluation was based on the realization of mechanical characterization tests and amicrostructural characterization.The mechanical tests for characterization at high temperatures were carried out in a transientregime, in which the specimen is placed in tension with constant load and heated at a constant speed untilfailure. Temperature and total strain are measured during the test and the results are converted to stressstraincurves.Microstructural characterization and hardness measurements were performed to explain the tensilebehavior of specimens after exposure to high temperatures, using optical microscopy techniques to performmetallographic studies.The results were compared. This comparison was performed by analyzing the results of stress andextension diagrams of tests carried out on specimens, confronting the steel strength parameters, with regardto the behavior of the material in question. From the results of this study, it was possible to understand thebehavior of metallic specimens when exposed to heating situations.Based on the stress-strain curves at a specific temperature, the mechanical parameters and reductionfactors were determined and were compared with the results obtained with several authors and with thestandards EN 1993 1-2, Australian Standard (Australian Code) and British Standard (British Code).This study revealed that the yield strength of the welds gradually decreased with increasingtemperature. A comparison compared a similarity between the curve of yield stress reduction factors forthe steel under study associated with a melting of 1.5 and 2.0% and the curve recommended by EN 1993-1-2: 2010 (2010) for hot-rolled grade 4 steels used. While the curve of yield stress reduction factors for thesteel under study associated with ingredients of 0.2% and 0.5% was similar to the curve recommended bythe British standard (BS 5950-8).
Description: Dissertação de Mestrado em Construção Metálica e Mista apresentada à Faculdade de Ciências e Tecnologia
URI: http://hdl.handle.net/10316/97980
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado

Show full item record

Page view(s)

7
checked on Aug 12, 2022

Download(s)

4
checked on Aug 12, 2022

Google ScholarTM

Check


This item is licensed under a Creative Commons License Creative Commons