Título: | Adhesion failures on hard coatings induced by interface anomalies | Autor: | Silva, Carlos W. Moura e Alves, E. Ramos, A. R. Sandu, Cosmin S. Cavaleiro, A. |
Palavras-chave: | DLC coatings; Adhesion; Contamination layer; Ion cleaning | Data: | 16-Jun-2009 | Editora: | Elsevier Ltd. | Citação: | Vacuum. 83:10 (2009) 1213-1217 | Resumo: | In this work, the lack of adhesion occurred during the up-scaling of the deposition of tribological coatings in a semi-industrial apparatus is interpreted. The adhesion problems were detected for both hard and self-lubricant coatings from W-Ti-N and W:C systems, respectively, when they were deposited in a 4 cathodes TEER® chamber by reactive unbalanced magnetron sputtering. In spite of cleaning the substrates surface by ion bombardment prior to deposition, by establishing a discharge close to the substrate, insufficient adhesion critical load values were measured by scratch-testing. A powerful set of complementary techniques was used to the detailed analysis of the interfaces in order to understand and overcome the adhesion problems: RBS gave some insights on the nature of the problem by detecting composition anomalies in the substrate/coating interface; Auger spectroscopy was used for identifying the underneath chemical composition close to the interface; cross section TEM gave the final evidence of the presence of a contamination layer attributed to malfunctioning of the ion cleaning process, which was the cause of the lack of adhesion | URI: | https://hdl.handle.net/10316/12887 | ISSN: | 0042-207X | DOI: | 10.1016/j.vacuum.2009.03.010 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Adhesion failures on hard coatings induced.pdf | 468.96 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
21
Visto em 15/abr/2024
Citações WEB OF SCIENCETM
18
Visto em 2/abr/2024
Visualizações de página 50
460
Visto em 16/abr/2024
Downloads 50
566
Visto em 16/abr/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.